Material | Sizes | Connection |
---|---|---|
Titanium | 1/2" to 42" | Welding |
Types | Equipment | Dimensions |
|
|
|
Manufacturing process | Certificates | Schedule |
|
EN 10204/3.1B Third Party Inspection report |
SCH5, SCH10, SCH20, SCH30, STD SCH40, SCH60, XS, SCH 80, SCH 100, SCH 120, SCH 140, SCH 160, XXS |
Origin | Bending Radius | Manufacturing types |
Ukraine / Korean / Japanese / Russian/ USA / European / Indian | 10D / 6D / 8D / 5D / 2D / 3D / 1D | ERW / Seamless / Welded | Raw Materials Certificate
Surface finish | End type | Delivery time |
|
|
USA : 28 - 67 days UK : 27 - 29 days Canada: 6 - 12 days |
Titanium grade 2 Welded fittings
Titanium Eccentric reducer
UNS N56400 1d elbow
Titanium grade 2 180 degree elbow
ASTM B363 Grade 5 Tee
ASTM B363 Gr WPT5 Stub End
Titanium Grade 5 Short radius elbow
Ti gr 5 6d elbow
DIN 3.7165 pipe fittings
Ti Alloy Gr 2 Long radius elbow
UNS R50400 buttweld fittings
DIN 3.7035 Cap
UNS R50400 3d elbow
ASTM B363 Gr WPT5 10d elbow
Ti alloy Grade 5 5d elbow
Titanium grade 5 4d elbow
Titanium buttweld fittings
Ti alloy 2d elbow
Titanium grade 5 Reducer
UNS N56400 Equal Cross
ASTM B363 gr 2 1.5d elbow
Ti alloy 90 degree elbow
ASTM B363 Grade WPT2 45 Degree elbow
ASTM B363 gr 2 buttweld fittings
Ti alloy Grade 5 Concentric reducer
DIN 3.7035 Seamless fittings
Ti gr 5 Reducing Tee
NPS in Centimeter |
O.D. In MM | 90 Degree Elbow | 45 Degree Elbow |
Buttweld Tee | Buttweld Cap | |
---|---|---|---|---|---|---|
Long Radius A |
Short Radius A |
B | C | E | ||
1.27 | 21.336 | 1-1/2 | – | 5/8 | 1 | 1 |
1.905 | 26.67 | 1-1/8 | – | 7/16 | 1-1/8 | 1-1/4 |
1 | 33.401 | 1-1/2 | 1 | 7/8 | 1-1/2 | 1-1/2 |
2.54 | 42.164 | 1-7/8 | 1-1/4 | 1 | 1-7/8 | 1-1/2 |
2.54 | 48.26 | 2-1/4 | 1-1/2 | 1-1/8 | 2-1/4 | 1-1/2 |
5.08 | 60.325 | 3 | 2 | 1-3/8 | 2-1/2 | 1-1/2* |
5.08 | 73.025 | 3-3/4 | 2-1/2 | 1-3/4 | 3 | 1-1/2 |
7.62 | 88.9 | 4-1/2 | 3 | 2 | 3-3/8 | 2* |
7.62 | 101.6 | 5-1/4 | 3-1/2 | 2-1/4 | 3-3/4 | 2-1/2* |
10.16 | 114.3 | 6 | 4 | 2-1/2 | 4-1/8 | 2-1/2* |
12.7 | 141.3002 | 7-1/2 | 5 | 3-1/8 | 4-7/8 | 3* |
15.24 | 168.275 | 9 | 6 | 3-3/4 | 5-5/8 | 3-1/2* |
20.32 | 219.075 | 12 | 8 | 5 | 7 | 4* |
25.4 | 273.05 | 15 | 10 | 6-1/4 | 8-1/2 | 5* |
30.48 | 323.85 | 18 | 12 | 7-1/2 | 10 | 6* |
35.56 | 355.6 | 21 | 14 | 8-3/4 | 11 | 6-1/2* |
Grade | Ti | C | Fe | H | N | O | Al | V |
---|---|---|---|---|---|---|---|---|
Grade2 | 99.2 min | 0.1 max | 0.3 max | 0.015 max | 0.03 max | 0.25 max | - | - |
Grade5 | 90 min | - | 0.25 max | - | - | 0.2 max | 6 min | 4 min |
Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
---|---|---|---|---|---|
Grade2 | 4.5 g/cm3 | 1665 °C (3030 °F) | Psi – 49900 , MPa – 344 | Psi – 39900 , MPa – 275 | 20 % |
Grade5 | 4.43 g/cm3 | 1632 °C (2970 °F) | Psi – 138000 , MPa – 950 | Psi – 128000 , MPa – 880 | 14 % |
Grade | WERKSTOFF NR. | UNS |
---|---|---|
Grade2 | 3.7035 | R50400 |
Grade5 | 3.7165 | N56400 |